Structures by: Georgiev P. A.
Total: 13
La (Ni3.55 Co0.75 Mn0.4 Al0.3) D4.83
Al0.3Co0.75D4.83LaMn0.4Ni3.55
Journal of Alloys Compd. (2003) 349, 325-333
a=5.333Å b=5.333Å c=4.248Å
α=90° β=90° γ=120°
La (Ni3.49 Co0.78 Mn0.42 Al0.31) D4.31
Al0.31Co0.78D4.31LaMn0.42Ni3.49
Journal of Alloys Compd. (2003) 349, 325-333
a=5.339Å b=5.339Å c=4.246Å
α=90° β=90° γ=120°
C16H10CuN4O4
C16H10CuN4O4
CrystEngComm (2019) 21, 43 6523
a=13.5518(4)Å b=13.9161(4)Å c=14.8283(4)Å
α=90° β=90.716(3)° γ=90°
C16H12CuN4O5
C16H12CuN4O5
CrystEngComm (2019) 21, 43 6523
a=14.251(2)Å b=13.399(2)Å c=14.6369(19)Å
α=90° β=93.001(11)° γ=90°
C33H24Cu2N8O9
C33H24Cu2N8O9
CrystEngComm (2019) 21, 43 6523
a=13.7136(4)Å b=13.2270(5)Å c=15.1795(5)Å
α=90° β=93.415(3)° γ=90°
C16H12CuN4O5
C16H12CuN4O5
CrystEngComm (2019) 21, 43 6523
a=13.8663(4)Å b=13.2350(4)Å c=15.0241(4)Å
α=90° β=93.199(2)° γ=90°
C32H20Cu2N8O10
C32H20Cu2N8O10
CrystEngComm (2019) 21, 43 6523
a=14.5493(3)Å b=11.93948(14)Å c=14.1517(3)Å
α=90° β=93.6939(5)° γ=90°
C160H80N8O48Zn8,13(C3H4NO)
C160H80N8O48Zn8,13(C3H4NO)
CrystEngComm (2013) 15, 45 9408
a=14.8149(18)Å b=54.114(6)Å c=9.2584(12)Å
α=90.00° β=110.055(9)° γ=90.00°
C40H24BrN2O13Zn2,5(C3H7NO)
C40H24BrN2O13Zn2,5(C3H7NO)
CrystEngComm (2013) 15, 45 9408
a=9.2506(6)Å b=14.4032(10)Å c=27.384(2)Å
α=97.587(6)° β=93.139(6)° γ=106.920(5)°
C24H23.7ClIn3N3O20.35
C24H23.7ClIn3N3O20.35
Chemistry of Materials (2016) 28, 20 7353
a=22.4570(3)Å b=22.4570(3)Å c=22.4570(3)Å
α=90.00° β=90.00° γ=90.00°
C24H15ClFe3N3O16
C24H15ClFe3N3O16
Chemistry of Materials (2016) 28, 20 7353
a=21.8720(9)Å b=21.8720(9)Å c=21.8720(9)Å
α=90.00° β=90.00° γ=90.00°
C24H25.5BrIn3N3O21.25
C24H25.5BrIn3N3O21.25
Chemistry of Materials (2016) 28, 20 7353
a=22.4530(4)Å b=22.4530(4)Å c=22.4530(4)Å
α=90.00° β=90.00° γ=90.00°
C24H9Fe3N3O16
C24H9Fe3N3O16
Chemistry of Materials (2016) 28, 20 7353
a=21.9524(6)Å b=21.9524(6)Å c=21.9524(6)Å
α=90° β=90° γ=90°